Microstructural Characterization of ULC Steel

In the present study, microstructure of the ULC steel was investigated by using the X-ray diffraction (XRD), optical microscopy (OM) and electron back scattering diffraction (EBSD) analysis. The pure ferrite phase consisting of various crystalline orientations, e.g. (110) and (200) etc., existed in the ULC steel. Ultra-fine grains of ferrite were observed in the ND-TD cross-section (⊥ RD), meanwhile, typical lamina were seen in the ND-RD cross-section (// RD) of the steel sheet. Grain size of the annealed steel was observed to be coarser and equiaxed in all direction. According the EBSD results, intensities of the beneficial texture {111}<001> increased in the annealed steel, but weakened in the cross-section that was parallel to rolling direction. Ratio of low-angle grain boundaries (1°< LAGBs < 15°) in the annealed steel was estimated as the higher value (93.1 %) than that in the cold-rolled steel (69.1 %).